Evaluation and comparison of surface characteristics of commercially available TMA wires using scanning electron microscopy and optical profilometer.

AIM: The aim of this study was to evaluate and compare the surface characteristics of colored titanium molybdenum alloy archwires (purple-coated TMA and honey dew-coated TMA) and the regular titanium molybdenum alloy archwires. MATERIALS AND METHODS: The experiment comprised three groups, Group I - regular TMA archwires, Group II - purple-coated TMA archwires, Group III - honey dew-coated TMA wires involving 21 samples each. The surface characteristics were assessed using scanning electron microscopy and optical profilometer. RESULTS: The results were statistically analyzed using analysis of variance wherein Group I regular TMA wires exhibited a root mean square value of 148.071 nm and a standard deviation of 9.0027 nm followed by group II (purple-coated TMA wires) which showed a root mean square value of 84.095 nm with a standard deviation of 2.6005 nm, while group III (honey dew-coated TMA wires) was found to have a root mean square value of 71.681 nm with a standard deviation of 1.4645 nm on subjecting to optical profilometry. CONCLUSION: The surface roughness is higher for regular TMA wire exhibiting superior characteristic of color-coated TMA wires, especially honey dew-coated TMA wires over the regular and purple-coated TMA wires. This property of the archwires details regarding its application in both sliding and frictionless mechanics in retraction phase of fixed orthodontic treatment.